pc ‖德国拜耳‖ 8025 ul认证：

bayer materialscience ag

chempark, gebaeude b207, leverkusen 51368 de

8025 + (z)

polycarbonate (pc), "makrolon", furnished as pellets

   min thk    flame            rti    rti    rti

color    (mm)    class    hwi    hai    elec    imp    str

all    1.5    v-2    5    4    125    115    125

   3.0    v-2    4    4    125    115    125

   6.0    v-1    4    4    125    115    125

comparative tracking index (cti):    -    inclined plane tracking (ipt):    -

dielectric strength (kv/mm):    -    volume resistivity (10x ohm-cm) :    -

high-voltage arc tracking rate (hvtr):    4    high volt, low current arc resis (d495):    -

dimensional stability (％):    -        

(z) -     material designation【敏感词】color code may be followed by up to three letters and/or three numbers (does not include grades which are separately recognized with above material designation【敏感词】suffix)

+ -     material designations may be followed by a six digit numerical code denoting color.

ansi/ul 94 small-scale test data does not pertain to building materials, furnishings【敏感词】related contents. ansi/ul 94 small-scale test data is intended solely for determining the flammability of plastic materials used in the components【敏感词】parts of end-product devices【敏感词】appliances, where the acceptability of the combination is determined by ul.

report date: 1972-09-28

last revised: 2011-12-12    ? 2014 ul llc    

iec【敏感词】iso test methods

           thickness    

test name    test method    units    tested (mm)    value

flammability    iec 60695-11-10    class (color)    1.5    v-2 (all)

           3.0    v-2 (all)

           6.0    v-1 (all)

glow-wire flammability (gwfi)    iec 60695-2-12    c    -    -

glow-wire ignition (gwit)    iec 60695-2-13    c    -    -

iec comparative tracking index    iec 60112    volts (max)    -    -

iec ball pressure    iec 60695-10-2    c    -    -

iso heat deflection (1.80 mpa)    iso 75-2    c    -    -

iso tensile strength    iso 527-2    mpa    -    -

iso flexural strength    iso 178    mpa    -    -

iso tensile impact    iso 8256    kj/m2    -    -

iso izod impact    iso 180    kj/m2    -    -

iso charpy impact    iso 179-2    kj/m2    -    -

makrolon® 8025

聚碳酸  酯

20％ 带压花的玻璃纤维

bayer materialscience - polycarbonates

产品说明:

mvr (300 °c/1.2 kg) 6.0 cm3/10 min; 20 ％ glass fiber reinforced; high viscosity; easy release; extrusion; injection molding - melt temperature 310 - 330 °c; vailable in opaque colors only; precision parts

总体  

材料状态  已商用：当前有效

资料 1  technical datasheet (chinese (traditional))

technical datasheet (chinese)

technical datasheet (english)

technical datasheet (german)

ul 黄卡 2  e41613-233157

搜索 ul 黄卡  bayer materialscience - polycarbonates

makrolon®

供货地区  北美洲

非洲和中东

拉丁美洲

欧洲

亚太地区

填料/增强材料  带压花的玻璃纤维, 20％ 填料按重量

特性  脱模性能良好

粘度，高

rohs 合规性  rohs 合规

外观  不透明

形式  粒子

多点数据  creep modulus vs. time (iso 11403-1)

isochronous stress vs. strain (iso 11403-1)

isothermal stress vs. strain (iso 11403-1)

secant modulus vs. strain (iso 11403-1)

shear modulus vs. temperature (iso 11403-1)

viscosity vs. shear rate (iso 11403-2)

物理性能 额定值 单位制 测试方法

密度 1.34 g/cm3 iso 1183

表观密度 3 0.69 g/cm3 iso 60

熔流率（熔体流动速率） (300°c/1.2 kg) 6.5 g/10 min iso 1133

溶化体积流率（mvr） (300°c/1.2 kg) 6.00 cm3/10min iso 1133

收缩率      

垂直流动方向 0.30 到 0.45 ％ iso 2577

流动方向 0.30 到 0.45 ％ iso 2577

垂直流动方向 : 2.00 mm 4 0.35 ％ iso 294-4

流动方向 : 2.00 mm 4 0.55 ％ iso 294-4

吸水率     iso 62

饱和, 23°c 0.24 ％  

平衡, 23°c, 50％ rh 0.10 ％  

硬度 额定值 单位制 测试方法

球压硬度 136 mpa iso 2039-1

机械性能 额定值 单位制 测试方法

拉伸模量 (23°c) 4000 mpa iso 527-2/1

拉伸应力      

屈服, 23°c 58.0 mpa iso 527-2/50

断裂, 23°c 50.0 mpa iso 527-2/5

拉伸应变      

屈服, 23°c 3.5 ％ iso 527-2/50

断裂, 23°c 6.5 ％ iso 527-2/5

拉伸蠕变模量     iso 899-1

1 hr 3700 mpa  

1000 hr 3500 mpa  

弯曲模量 5 (23°c) 3700 mpa iso 178

弯曲应力 5     iso 178

3.5％ 应变, 23°c 95.0 mpa  

23°c 100 mpa  

flexural strain at flexural strength 6 (23°c) 5.4 ％ iso 178

冲击性能 额定值 单位制 测试方法

简支梁缺口冲击强度 7 (23°c, 完全断裂) 12 kj/m2 iso 179/1ea

简支梁无缺口冲击强度     iso 179/1eu

-60°c, 完全断裂 65 kj/m2  

-30°c, 完全断裂 65 kj/m2  

23°c, 完全断裂 55 kj/m2  

悬壁梁缺口冲击强度 8 (23°c, 完全断裂) 12 kj/m2 iso 180/a

多轴向仪器化冲击能量     iso 6603-2

-30°c 10.0 j  

23°c 20.0 j  

多轴向仪器化冲击力峰值     iso 6603-2

-30°c 2800 n  

23°c 3300 n  

热性能 额定值 单位制 测试方法

热变形温度      

0.45 mpa, 未退火 141 °c iso 75-2/b

1.8 mpa, 未退火 134 °c iso 75-2/a

维卡软化温度      

-- 146 °c iso 306/b50

-- 147 °c iso 306/b120

ball pressure test (137°c) pass   iec 60695-10-2

线形热膨胀系数     iso 11359-2

流动 : 23 到 55°c 4.5e-5 cm/cm/°c  

横向 : 23 到 55°c 5.5e-5 cm/cm/°c  

导热系数 9 (23°c) 0.23 w/m/k iso 8302

rti elec (1.50 mm) 125 °c ul 746

rti imp (1.50 mm) 115 °c ul 746

rti (1.50 mm) 125 °c ul 746

电气性能 额定值 单位制 测试方法

表面电阻率 1.0e+16 ohm iec 60093

体积电阻率 (23°c) 1.0e+16 ohm·cm iec 60093

介电强度 (23°c, 1.00 mm) 36 kv/mm iec 60243-1

相对电容率     iec 60250

23°c, 100 hz 3.30    

23°c, 1 mhz 3.30    

耗散因数     iec 60250

23°c, 100 hz 1.0e-3    

23°c, 1 mhz 9.0e-3    

漏电起痕指数     iec 60112

解决方案 a 175 v  

解决方案 b 125 v  

可燃性 额定值 单位制 测试方法

ul 阻燃等级     ul 94

1.50 mm v-2    

6.00 mm v-1    

灼热丝易燃指数     iec 60695-2-12

0.750 mm 800 °c  

1.50 mm 960 °c  

2.00 mm 960 °c  

3.00 mm 960 °c  

4.00 mm 960 °c  

热灯丝点火温度     iec 60695-2-13

0.750 mm 850 °c  

2.00 mm 875 °c  

3.00 mm 875 °c  

极限氧指数 10 32 ％ iso 4589-2

application of flame from small burner 11 (2.00 mm) k1, f1   din 53438-1, -3

burning rate 12 (< 1.00 mm) passed   iso 3795

flash ignition temperature 470 °c astm d1929

needle flame test     iec 60695-11-5

method f : 1.50 mm 2.0 min  

method f : 2.00 mm 2.0 min  

method f : 3.00 mm 2.0 min  

method k : 1.50 mm 1.0 min  

method k : 2.00 mm 1.0 min  

method k : 3.00 mm 2.0 min  

self ignition temperature 550 °c astm d1929

补充信息 额定值   测试方法

electrolytical corrosion a1   iec 60426

注射 额定值 单位制