· 特点：lnp* stat-loy* pom kx95702 是一种含有防静电的化合物聚甲  醛  树脂，这种材料的新增功能包括：抗静电剂  。

· lnp stat-loy pom kx95702

lnp™ stat-loy™ compound pom kx95702

also known as:lnp™ stat-loy™ compound pdx-k-95702 product reorder name:kx95702

lnp stat-loy* kx95702 is a compound based on acetal resin containing anti-static. added features of this material include: antistat.

property

typical properties(1)mechanicalvalueunitstandardtensile stress,yield410kgf/cm2astm d 638tensile stress,break250kgf/cm2astm d 638tensile strain,yield18.1％astm d 638tensile strain,break75.5％astm d 638tensile modulus,50mm/min15300kgf/cm2astm d 638flexural stress470kgf/cm2astm d 790flexural modulus14100kgf/cm2astm d 790tensile stress,yield41mpaiso 527tensile stress,break31mpaiso 527tensile strain,yield14.6％iso 527tensile strain,break52.4％iso 527tensile modulus,1mm/min1110mpaiso 527flexural stress35mpaiso 178flexural modulus1350mpaiso 178impactvalueunitstandardizod impact,unnotched,23℃nbcm-kgf/cmastm d 4812izod impact,notched,23℃16cm-kgf/cmastm d 256instrumented impact energy @ peak,23℃230cm-kgfastm d 3763multiaxial impact168cm-kgfiso 6603izod impact,unnotched 80*10*4 +23℃nbkj/m2iso 180/1uizod impact,notched 80*10*4 +23℃14kj/m2iso 180/1athermalvalueunitstandardhdt,1.82 mpa,3.2mm,unannealed78℃astm d 648cte,-40℃ to 40℃,flow1.24e-041/℃astm e 831cte,-40℃ to 40℃,xflow1.39e-041/℃astm e 831cte,-40℃ to 40℃,flow1.24e-041/℃iso 11359-2cte,-40℃ to 40℃,xflow1.39e-041/℃iso 11359-2hdt/af,1.8 mpa flatw 80*10*4 sp=64mm64℃iso 75/afphysicalvalueunitstandarddensity1.32g/cm3astm d 792moisture absorption,50％ rh,24 hrs4.05％astm d 570mold shrinkage,flow,24 hrs(5)1.7％astm d 955mold shrinkage,xflow,24 hrs(5)1.8％astm d 955mold shrinkage,flow,24 hrs(5)1.74％iso 294mold shrinkage,xflow,24 hrs(5)1.83％iso 294electricalvalueunitstandardsurface resistivity1.e+09-1.e+11ohmastm d 257source gmd,last updated:2004/10/01 parameter injection moldingvalueunitdrying temperature80℃drying time4hrsmelt temperature195-205℃front-zone 3 temperature200-210℃middle-zone 2 temperature190-200℃rear-zone 1 temperature175-190℃mold temperature70-95℃back pressure0.2-0.3mpascrew speed30-60rpm